轻烧镁球 Light burned magnesium ball

http://www.ykbhlm.com    轻烧镁球是以轻烧氧化镁粉为原料，经压球机压制而成。该产品粒度均匀、机械强度高、活好、在高温炉渣中易分解熔化、便于操作，是转炉溅渣护炉理想的炉渣调节材料轻烧氧化镁球主要用做转炉溅渣护炉的护渣成分调节剂。因为溅渣护炉要求炉渣要有合适的粘度和耐火度，合理的炉渣成分是实施溅渣护炉的关键。一般的炉渣不能直接进行溅护炉，需要加入一定量的氧化镁球进行调节，同时代替白云石的使用，减少渣量，提高炉渣中MgO的含量。由于MgO是高熔点矿物，熔点2800℃，炉渣中MgO含量的提高，使炉渣粘度变大，耐火度提高，炉渣更容易与炉衬结合在一起，在炉衬上形成有效的炉渣保护层，从而提高炉衬寿命，降低消耗。

http://www.ykbhlm.com Light-burned magnesia ball is made from light-burned magnesia powder and pressed by ball press. The product has uniform particle size, high mechanical strength, good liveliness, easy decomposition and melting in high temperature slag, and easy operation. It is an ideal slag conditioning material for converter slag splash protection. Light-burned magnesium oxide balls are mainly used as slag protection for converter slag splash protection. Ingredient modifiers. Because the slag splashing furnace requires proper slag viscosity and fire resistance, reasonable slag composition is the key to the slag splashing furnace. General slag can not be directly splash-protected. It is necessary to add a certain amount of magnesia balls for adjustment, and instead of using dolomite, reduce the amount of slag and increase the content of MgO in the slag. As MgO is a high melting point mineral with a melting point of 2800 ° C and an increase in the content of MgO in the slag, the viscosity of the slag becomes larger and the fire resistance is improved. The slag is more easily combined with the lining, and an effective slag protective layer is formed on the lining, thereby improving the lining. Life and reduce consumption.